Filamentos elásticos de elastolefina de alta durabilidad obtenidos a partir de copolímeros de bloque de etileno-octeno de baja densidad mediante la tecnología de polimerización por transferencia de cadena para aplicaciones en indumentaria de uso profesional

Author

Verdú Blasco, Pau

Director

Cayuela Marín, Diana

Date of defense

2010-10-29

Legal Deposit

B. 28456-2012

Pages

479 p.



Department/Institute

Universitat Politècnica de Catalunya. Departament d'Enginyeria Tèxtil i Paperera

Abstract

En la actualidad el mercado carece de prendas elásticas para uso profesional puesto que los elastanos habitualmente utilizados son inestables frente a altas temperaturas y químicos agresivos, e.g. termofijado, mantenimiento de indumentaria industrial etc. Recientemente se han venido utilizado filamentos olefínicos obtenidos a partir de copolímeros al azar de etileno-octeno (Dow XLA™ fibers producidos por The Dow Chemical Company). Aunque más resistentes a las temperaturas debido a la reticulación, su bajo punto de fusión, alrededor de 50ºC, limita el comportamiento elástico en tejidos pesados y tupidos para indumentaria profesional. La investigación tiene por objeto la obtención de monofilamentos elásticos a partir copolímeros de bloque de etileno-octeno (cuyo punto de fusión es más elevado) y con éstos, tejidos para indumentaria profesional que ofrezcan mayor fuerza de encogimiento a las temperaturas típicas de los pre-tratamientos, tintura y acabado (50ºC-120ºC). El objetivo es hacer que los tejidos encojan más durante las operaciones en húmedo bajo temperatura para mejorar así su elasticidad y aumentar el peso en comparación con los tejidos actuales manufacturados con los convencionales copolímeros homogéneos de etileno-octeno reticulados Los tejidos deberán garantizar las siguientes propiedades durante todo su ciclo de vida: estabilidad dimensional, relación elasticidad-crecimiento mejorado, resistencia química, resistencia térmica, durabilidad ante los lavados industriales y un mejor confort termofisiológico y sensorial.


Due to the lack of stability of elastane based materials against high temperatures and harsh chemicals, e.g. thermofixation and professional wear maintenance, elastic garments with elastane content are not yet fully commercial products. The Dow Chemical Company has recently commercialized a random ethylene-octene copolymer based fiber named Dow XLA™ fiber. Despite its higher temperature resistance as one of the crosslinking effects, its very low melting point, around 50ºC, establishes some limitations in elasticity such in heavy weight and high densely woven fabric cases typically found in professional wear applications. The target for the investigation is to produce block ethyleneoctene copolymer based filaments in which the melting point is supposed to be higher than in random copolymer materials. Different workwear fabrics will be manufactured with yarns containing such elastic filaments. It is supposed these fabrics to show high shrinkage forces even at dyeing and finishing temperatures, (50ºC-120ºC). The goal is to produce fabrics with superior shrinkage performance in order to achieve an excellent elastic power and the final desired fabric weight. Properties such as dimensional stability, stretch and growth ratio, temperature and chemical resistance and durability against industrial laundering should not be affected by the passage of the time. To validate this point these properties will be measured in the fabrics off loom and after the garment cycle life. These fabrics are also supposed to show better thermophysiological and sensorial properties than random copolymer fiber based textiles

Keywords

etileno-octeno; elastolefina; block copolymer; copolímero de bloque; filamento elástico; elastic filament; tejido elástico; elastic fabric; ethylene-octene; elastolefin

Subjects

67 - Various industries, trades and crafts

Documents

TPVB1de1.pdf

9.108Mb

 

Rights

ADVERTIMENT. L'accés als continguts d'aquesta tesi doctoral i la seva utilització ha de respectar els drets de la persona autora. Pot ser utilitzada per a consulta o estudi personal, així com en activitats o materials d'investigació i docència en els termes establerts a l'art. 32 del Text Refós de la Llei de Propietat Intel·lectual (RDL 1/1996). Per altres utilitzacions es requereix l'autorització prèvia i expressa de la persona autora. En qualsevol cas, en la utilització dels seus continguts caldrà indicar de forma clara el nom i cognoms de la persona autora i el títol de la tesi doctoral. No s'autoritza la seva reproducció o altres formes d'explotació efectuades amb finalitats de lucre ni la seva comunicació pública des d'un lloc aliè al servei TDX. Tampoc s'autoritza la presentació del seu contingut en una finestra o marc aliè a TDX (framing). Aquesta reserva de drets afecta tant als continguts de la tesi com als seus resums i índexs.

This item appears in the following Collection(s)